Table of Mechanical Properties (ASTM) for Titanium Bar & Billet

tensile Strength, min

yield Strength
(0.2%offset)
min or range

elongation In 4d

reduction Of area

grade

ksi

mpa

ksi

mpa

min.%

min.%

1

35

240

20

138

24

30

2

50

345

40

275

20

30

2h

58

400

40

275

20

30

3

65

450

55

380

18

30

4

80

550

70

483

15

25

5

130

895

120

828

10

25

6

120

828

115

795

10

25

7

50

345

40

275

20

30

7h

58

400

40

275

20

30

9

90

620

70

483

15

25

9i

90

620

70

483

12

25

11

35

240

20

138

24

30

12

70

483

50

345

18

25

13

40

275

25

170

24

30

14

60

410

40

275

20

30

15

70

483

55

380

18

25

16

50

345

40

275

20

30

16h

58

400

40

275

20

30

17

35

240

25

170

24

30

18

90

620

70

483

15

25

18i

90

620

70

483

12

20

19ii

115

793

110

759

15

25

19iii

135

930

130 to 159

897 to 1096

10

20

19e

165

1138

160 to 185

1104 to 1276

5

20

20ii

115

793

110

759

15

25

20iii

135

930

130 to 159

897 to 1096

10

20

20iv

165

1138

160 to 185

1104 to1276

5

20

21ii

115

793

110

759

15

35

21iii

140

966

130 to 159

897 to 1096

10

30

21iv

170

1172

160 to 185

1104 to 1276

8

20

23

120

828

110

759

10

15

23i

120

828

110

759

7.5 v,6.0vi

25

24

130

895

120

828

10

25

25

130

895

120

828

10

25

26

50

345

40

275

20

30

27

35

240

25

170

24

30

28

90

620

70

483

15

25

28i

90

620

70

483

12

20

29

120

828

110

759

10

25

29i

120

828

110

759

7.5 v,6.0vi

15

30

50

345

40

275

20

30

31

65

450

55

380

18

30

32

100

689

85

586

10

25

33

50

345

40

275

20

30

34

65

450

55

380

18

30

35

130

895

120

828

5

20

36

65

450

60 to 95

410 to 655

10

 

37

50

345

31

215

20

30

38

130

895

115

794

10

25

above Properties apply to longitudinal sections up to 3 inch thickness With maximum of 10 inch. Mechanical properties of larger Sections shall be negotiated between the manufacturer and Purchaser.

i) Properties for material in transformed-beta condition.

ii) Properties for solution treated condition.

iii) Properties for solution treated and aged condition-moderate Strength (determined by aging temperature).

iv) Properties for solution treated and aged condition-high Strength (determined by aging temperature).

v) For product section or wall thickness values < 1.0 in.

vi) For product section or wall thickness values_> 1.0 in.

** While this information has been compiled with care, it is for convenience and for reference only and we assume no liability for any decisions based on the content therein.  it shall be your responsibility to ensure that any information in this document or on our website meets your specific requirements. **